TZM offers twice the strength of pure molybdenum at temperatures over 1300'C. The recrystallization temperature of TZM is approximately 250'C higher than molybdenum
TZM giver dobbelt styrke af ren molybd? n ved temperaturer over 1300'C. Den omkrystallisering temperatur TZM er ca 250'C h?

The recrystallization temperature of TZM is approximately 250'C higher than molybdenum
Den omkrystallisering temperatur TZM er ca 250'C h?

It is applied to remove water from substances in the production of perfume(especially artificial musk), for recrystallization of chemicals and as denaturant in spirit.
Det bruges til at fjerne vand fra stoffer i fremstilling af parfume(specielt kunstig musk), til rekrystallisering af kemikalier og som denatureringsmiddel i sprit.

soluble material dissolves and recrystallization to process inorganic synthesis and material.
opløseligt materiale opløse og omkrystallisere for at behandle uorganisk syntese og materiale.

The results also show, La 3 content will be from 1% to 4%, the recrystallization temperature of molybdenum doped from 1300℃ up to 2000℃.
Resultaterne viser også, vil La 3 indholdet være fra 1% til 4%, den omkrystallisering temperatur molybdæn dopet fra 1300 ℃ op til 2000 ℃.

Besides shrinkage, recovery(change of subgrain structures and strain relief), recrystallization(formation of strain free crystals low in dislocation density),
Udover svind, nyttiggørelse(ændring af subgrain strukturer og trækaflastning), omkrystallisering(dannelse af stamme gratis krystaller lavt dislokationsdensitet),

rare earth after recrystallization temperature of molybdenum increased about 500℃,
sjældne jordarter efter omkrystallisation temperatur molybdæn steg ca. 500 ℃,

TZC alloy(Titanium Zirconium Carbon Molybdenum) having excellent high temperature strength and high recrystallization temperature, and vacuum arc melting of powder metallurgy production method also has a good plasticity at room temperature.
TZC legering(Titanium Zirkonium Carbon Molybdæn) med fremragende høj temperatur styrke og høj omkrystallisering temperatur og vakuum bue smeltning af pulvermetallurgi produktionsmetode har også en god plasticitet ved stuetemperatur.

Reply TZM alloy(titanium zirconium molybdenum) complete recrystallization two grain growth process, from long fibrous tissue becomes equiaxed grains,
Svar TZM legering(titan zirconium molybdæn) omkrystallisation to hele kornet vækstproces, fra lange fibrøst væv bliver ligeakset kerner, mens TZM legering væsentligt forbedret sejhed,

direction TYM molybdenum alloy recrystallization temperature and high temperature performance there is a very significant impact,
retning TYM molybdæn legeret omkrystallisering temperatur og temperatur ydeevne høj er der en meget betydelig indvirkning,

The results showed that: wire annealed at 1750℃ for 30 minutes to form a long and large recrystallization, its tensile strength and bending performance is much better than the pure molybdenum, good room-temperature toughness.
Resultaterne viste, at: wire glødet ved 1750 ℃ i 30 minutter til dannelse af en lang og stor omkrystallisation, dens trækstyrke og bøjning ydeevne er meget bedre end den rene molybdæn, god stuetemperatur sejhed.

Grains of pure molybdenum occurs at 1 200℃ recrystallization from processing state fibrous tissue becomes equiaxed organizations,
Korn af ren molybdæn sker på en 200 ℃ omkrystallisering fra behandlingsstatus fibrøst væv bliver ligeakset organisationer, 1 400 ℃ når kornet til at vokse betydeligt,

the fine dispersed Ti-carbides are responsible for the excellent strength properties at temperatures up to 1400°C. The recrystallization temperature of TZM alloy is approximately 250°C higher than moly
de fine spredte Ti-karbider er ansvarlige for den fremragende styrkeegenskaber ved temperaturer op til 1400 ° C. Den omkrystallisering temperatur TZM er ca 250 ° C højere

such as high recrystallization temperature, high strength,
så højt omkrystallisation temperatur, høj styrke,

the recrystallization temperature of up to 1800, even after recrystallization still has some strength,
det omkrystallisering temperatur på op til 1800, selv efter omkrystallisation har stadig noget styrke,

other mechanical properties of little change, but in the recrystallization phase, significantly decreased strength,
andre mekaniske egenskaber ved en lille ændring, men i den omkrystallisering fase, faldt betydeligt styrke,

eventually forming a large aspect ratio of the lap tissue to improve the toughness of the material after recrystallization, and the recrystallization temperature is increased significantly.
efterhånden danner et stort formatforhold lap væv for at forbedre sejheden af materialet efter omkrystallisation, og omkrystallisation temperaturen forøges betydeligt.

then be processed by recrystallization.
derefter behandles ved omkrystallisation.

the temperature is still below the recrystallization range. Accordingly,
temperaturen er stadig under omkrystallisering interval. derfor,

Recrystallization temperature of molybdenum wire is significantly higher than the recrystallization temperature of pure molybdenum,
Omkrystallisering temperatur molybdæn er væsentligt højere end omkrystallisering temperatur af ren molybdæn,